Building Pads Shoed Rubber Products

Main Article Content

Atita Repadis
Peerachart Phanomrat
Natamon Noisri
Ausda Lamkomolvilas

Abstract

The  objectives  of  this  research  were  to  : 1)  create  the  pads  shoes  from  rubber  product for  walker  standing  in  five  to  ten  hours  2)  study  efficiency  of  the  pads  shoes  from rubber  product  for  denseness  and  3)  study users’  satisfactions  for  using  pads  shoes  from rubber  product.  The  samples  consisted  of  80 people  in  Khanjanaburi  Vocational  College  who used  the  pads  shoes  from  rubber  product.


The  result  of  the  study  were  as  follows: 1)  the  creation  of  20%  of  Potassium  Oleate to  effect  the  pads  shoes  from  rubber  product  appropriate  amount  were  14  grams  and  make them  stay  well  while  pouring  in  plate  including  the  size  of  the  sponge  had  a resolution  the  filler  replaces  the  latex  to  effect  of  the  denseness  and  rehydration  in rubbers  was  higher  and  rubbers  were  smaller  2)  The  higher  density  and  resilience  by  20%  potassium  oleate  particles  can  press  rubber  particles  to  make  them  compact.  Tested  results  for  density  0.177  g/cm3,  recovery  capacity  34.2%  and  3)  users’  satisfactions  for  using  the  rubber  sheets  for  foot  healthy  at  3.70,  fourth the  pads  shoes  from  rubber  appropriate  at  3.60,  fifth  the  format  at  3.58,  finally  the overall  of  the  pads  shoes  from  rubber  at  3.63  was  at  high  level.

Article Details

How to Cite
Repadis, A., Phanomrat, P., Noisri, N., & Lamkomolvilas, A. (2018). Building Pads Shoed Rubber Products. Vocational Education Central Region Journal, 2(2), 58–62. Retrieved from https://so06.tci-thaijo.org/index.php/IVECJournal/article/view/246502
Section
Research Articles

References

1. บุญธรรม นิธิอุทัย. (2530). ยางธรรมชาติ ยางสังเคราะห์ และคุณสมบัติ. ปัตตานี: คณะวิทยาศาสตร์และเทคโนโลยีมหาวิทยาลัยสงขลานครินทร์ วิทยาเขตปัตตานี.

2. วราภรณ์ ขจรไชยกูล. (2531). กระบวนการผลิตภัณฑ์ยาง. หาดใหญ่: ศูนย์วิจัยยางสงขลา กรมวิชาการเกษตร.

3. สุรศักดิ์ เทพทอง. (2545). อิทธิพลของสารก่อเจลเสริมต่อการหดตัวและสมบัติของฟองน้ำยางธรรมชาติ. วิทยานิพนธ์วิทยาศาสตรมหาบัณฑิต สาขาเทคโนโลยีพอลิเมอร์ มหาวิทยาลัยสงขลานครินทร์.