Effect Counter Force on Workpiece Shrinkage in Sheet Metal Extrusine Process
Article Sidebar
Main Article Content
Abstract
The objectives of this research are 1) to study the influence of back pressure on workpiece quality in the sheet metal extrusion process. 2) To apply the finite element method in the analysis of the sheet metal forming process. The results indicate that the influence of back pressure on workpiece collapse in the sheet metal extrusion process, to the stress in the workpiece material at the radius edge of the cutting edge will be separated. The affect to the diffusion of hydrostatic stress of material in the shear strip area has dispersion value and spread into the worksheets easity. When setting 20 kN, it was found that the hole appear at the end of the rounded compression that cause of more materials, When the pressure was set at 60 kN, it was found that little bit appear at the end of the compression because the resistance of the pressure the material is greater. Which will cause the creation of compressive stress around the compression hole to decrease and cause die rolls to occur. The principle and material use of sheet metal extrusion process simulation by finite element method was found that the results of experimental and simulation are the same, accuratery corresponds to reality.
Article Details
This work is licensed under a Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 International License.
สงวนสิทธิ์ โดย สถาบันการอาชีวศึกษาภาคตะวันออกเฉียงเหนือ 1
306 หมู่ 5 ถนนมิตรภาพ หนองคาย-อุดรธานี ตำบลโพธิ์ชัย อำเภอเมืองหนองคาย จังหวัดหนองคาย 43000
โทร 0-4241-1445,0-4241-1447
ISSN : 3027-6861 (print) ISSN : 3027-687X (online)
References
สุทัศน์ ทิพย์ปรักมาศ, มาซาฮิโกะ จิน และมาซาโอะ มูราคาวา, “การวิเคราะห์การไหลของเนื้อวัสดุของรอยฉีกขาดในงานตัดไฟน์แบลงค์”, วารสารวิจัยและพัฒนา มจธ ปีที่ 30, 2550, หน้า 293 – 300.
สุริยา ประสมทอง และเกียรติพงศ์ อรรถัต, “การเพิ่มประสิทธภาพของการขึ้นรูปแผ่นโดยอาศัยความเค้นตกค้างและความหยาบของพื้นผิวด้วย กระบวนการขึ้นรูปทีละจุด (TPIF) ของโลหะชิ้นส่วนผสมอะลูมิเนียม”, [ออนไลน์]. เข้าถึงได้จาก https://ojs.kmutnb.ac.th/index.php/ijst/article/view/6059/pdf_389. สืบค้น 25 พฤศจิกายน 2566.
สุรวุฒิ ยะนิล, ชาญ ถนัดงาน และศิริศักดิ์ หาญชูวงศ์, “การวิเคราะห์หาแรงในการไฟน์แบลงก์โดยระเบียบวิธีไฟไนต์เอลิเมนต์”, วารสารวิชาการพระจอมเกล้าพระนครเหนือ ปีที่ 13, 2546, หน้า 52 – 58.
Bopit Bubphachot. “Microstructure Affecting Cutting Quality in Fine Blanking Process,” American Journal of Engineering and applied Sciences;2009. 2(4): 665-668.
Chatkaew Suriyapha, Suthep Yiemchaiyaphum and Bopit Bubphachot. (2010). “Die Radius Affecting Sheet Metal Extrusion Quality for Fine Blanking Process,” American Journal of Engineering and Applied Sciences;2010. 3(2): 476-481.
F. Maqbool and M.Bambach. “Experimental and numerical ininvestigation of the influence of process parameters in incremental sheet metal forming on residual stresses,” Journal of Manufacturing and Materials Processing; 2019. 3(2): 31.
Hirota, K. 2007. “Fabrication of micro-billet by sheet extrusion”. Journal of Materials Processing Technology, 191(1–3), 283–287.
K. Hirota, H. Yanaga, and K. Fukushima. “Experimental and Numerical Study on Blanking Process with Negative Clearance,” Journal of Solid Mechanics and Materials Engineering; 2009. 3(2): 247-255.
P.F. Zheng, L.C. Chan and T.C. Lee, “Numerical Analysis of the Sheet Metal Extrusion Process,” Finite Elements in Analysis and design; 2005. 42, 189-207.
Schuler, G. 1998. Metal Forming Handbook: Springer Berlin.
S.M.Najm and I. Paniti, “Predict the effects of forming tool characteristics on surface roughness of aluminum foil components formed by SPIF using ANN and SVR, ” International Journal of Precision Engineering and Manufacturing; 2021. 22: 13-26.
Suriyapha C., Rittidech S. and Bubphachot B. “Material Flow Behaviour on Fine Blanking Process for Sheet Metal Extrusion,” Asian International Journal of Science and Technology in Production and Manufacturing Engineering; 2011. 4(1): 77-80.
Sutasn Thipprakmas, Masahiko Jin and Masao Murakawa. “An Investigation of Material Flow Analysis in Fineblanking Process,” Journal of Materials Processing Technology; 2007. 192–193, 237–242.
Sutasn Thipprakmas, Masahiko Jin, Kanaizuka Tomokazu, Yamamoto Katsuhiro, and Masao Murakawa. “Prediction of Fineblanked Surface Characteristics Using the Finite Element Method (FEM),” Journal of Materials Processing Technology; 2008. 198, 391-398.
W.F. Fan and J.H. Li. “An Investigation on the Damage of AISI-1045 and AISI-1025 Steels in Fine-Blanking with Negative Clearance,” Materials Science and Engineering A; 2009. 499, 248-251.
Z.H. Chen, C.Y. Tang, L.C. Chan and T.C. Lee. “Simulation of the Sheet Metal Extrusion Process by the Enhanced Assumed Strain Finite Element Method,” Journal of Materials Processing Technology; 1999. 250-256.
Z. Zhao, X.C. Zhuang and X.l. Xie. “An Improved Ductile Fracture Criterion for Fine-blanking Process,” J. Shanghai Jiaotong Univ. (Sci.); 2008. 13(6), 702–706